Kinetyka przemian fazowych przy odpuszczaniu i jej wpływ na własności stali
(Data obrony: 2007-05-14) Bała, Piotr
Wydział Inżynierii Metali i Informatyki Przemysłowej
In the paper a description of phase transformations during continuous heating and isothermal holding from quenched state (tempering), its influence on properties of steel has been presented and the influence of development of selected phase transformations during tempering (by pre-tempering) on final properties of steel has been defined. The following sequence of phase transformations during tempering of test tool steels has been found: precipitation of carbide $\varepsilon$, precipitation of cementite within the range of which the retained austenite transforms, after that, in case of steels characterized by secondary hardness effect, independently nucleating carbides of $MC$ type and the subsequent $M_{2}C$ Separated carbides of $MC$ type remain in the structure exhibiting poor inclination for coagulation, while carbides of $M_{2}C$ type transform „in situ” into $M_{6}C$ and $M_{23}C_{6}$ carbides.It has been shown that development (by pre-tempering) of selected phase transitions during tempering may have an effect on steel properties after actual tempering. An advantageous influence of pre-tempering within the range of carbides $\varepsilon$ precipitation has been stated. The influence of the progress of cementite precipitation and transition of retained austenite may not be generalized for its strong dependence from chemical composition of the steel. However it is possible, using CHT (continuous heating transformations from quenched state) and ITH (isothermal holding transformations from quenched state) diagrams, to control both transformations in order to change desired properties of steel.
Access status: Restricted ,
Struktura i własności połączeń zgrzewanych stali i staliw stosowanych w kolejnictwie
(Data obrony: 2012) Parzych, Sławomir
Wydział Inżynierii Metali i Informatyki Przemysłowej
The main objectives of the work was to determine the effect of heat treatment on microstructure and properties of bainitic cast steel Lo8CrNiMo and demonstrating the possibility of producing correct resistance butt weld made of bainitic cast steel with currently used grades of rail steel 1200MnCrMoV20 and R260. Materials used nowadays in the railway industry for frogs: Hadfield cast steel (L120G13) and forged pearlitic steel (R260) do not fulfil strict conditions of exploitation and speed that should be reached on railway. One of the possible solutions is to use cast steel with bainitic or bainitic-martensitic microstructure, which allows to gain high strength. The test material is an alternative to railway frogs made of the Hadfield cast steel. In order to ensure similar wear in both the resistance butt weld and the base material, the resistance butt weld should have almost the same mechanical and tribological properties as the base metal. Thanks to using modern research methods, the heat treatment and welding technology for newly developed materials for railway crossovers were proposed in this study. Performed exploitation tests of bainitic cast steel showed that the cast can fully compete with currently used materials for the railway frogs, on which the traffic reaches the speed up to 200 km/h.
Access status: Restricted ,
Struktura i własności stali z niklem do ulepszania cieplnego
(Data obrony: 2006) Zając, Grzegorz
Wydział Inżynierii Metali i Informatyki Przemysłowej
Celem pracy było zbadanie wpływu niklu na kinetykę przemian fazowych przechłodzonego austenitu, kinetykę przemian przy odpuszczaniu oraz na strukturę i własności stali $Cr-Mo$ do ulepszania cieplnego o zmiennej zawartości niklu dla weryfikacji dotychczasowych ocen wpływu tego pierwiastka oraz stworzenia własnej bazy danych o ilościowym wpływie tego pierwiastka na własności stali. Badania wykonano na specjalnie w tym celu zaprojektowanych stopach modelowych stali $Cr-Mo$ do ulepszania cieplnego zawierających zróżnicowane zawartości niklu. Dylatometrycznie wyznaczono temperatury krytyczne przemian fazowych przy nagrzewaniu badanych stopów, opracowano wykresy kinetyki przemian fazowych przechłodzonego austenitu (CTPc) oraz wykresy kinetyki przemian przy ciągłym nagrzewaniu za stanu zahartowanego $(CTPc^{\circ})$. Do oceny mikrostruktury wykorzystano zarówno mikroskopię świetlną jak i transmisyjną mikroskopię elektronową. Oceny udziału austenitu szczątkowego dokonano przy pomocy rentgenowskiej ilościowej analizy fazowej. Badania własności mechanicznych obejmowały pomiary twardości, statyczną próbę rozciągania, badania udarności i odporności na pękanie KIc. Badania fraktograficzne przełomów próbek użytych do wyznaczenia współczynnika KIc wykonywano na skaningowym mikroskopie elektronowym.