(AGH University Press, 2023) Karwan-Baczewska, Joanna; Perek-Nowak, Małgorzata; Majchrowska, Magdalena; Rosso, Mario
The article discusses the effect of different particle fractions of prealloyed iron powder on the microstructure, density and hardness of sintered material. Each particle fraction (apart from 160-200 μm, which is a trace fraction) was modified with boron, its contents being, respectively, 0.2 wt.%, 0.4 wt.% and 0.6 wt.%. Next, the powder mixtures were pressed under a pressure of 600 MPa, and the final compacts were subject to sintering at 1200°C for 60 min in a hydrogen atmosphere. It was observed that the higher values of density and hardness were found in samples made from finer fractions of powder. A higher homogeneity of the microstructure and the highest degree of compactness was obtained in sinters from powder of 40-56 μm particle size, with 0.4 wt.% B. Due to the use of small particle fractions of prealloyed powder, a higher degree of compactness in sinters was obtained with lower boron content. Also indicated was which particle fraction of Fe-Ni-Mo-Cu powder should be applied to obtain density in sinters with boron addition equal to almost 100% of the relative density of the analyzed alloy. The presented studies have both scientific and technological aspects.