Montmorillonity podpierane polikationami cyrkonowymi jako sorbenty i katalizatory w ochronie środowiska

Abstract

Modification of sodium montmorillonite with zirconium polycations was carried out. As a result, a microporous, non-swelling, thermally stable structure was obtained. Such material can be used in environmental protection as a catalyst support in the removal of toxic volatile chlorinated organic compounds. The possibility of using Zr-PILC as a kind of storage for carbon dioxide was also examined. Thermal analysis combined with the analysis of the emitted gaseous products showed that this material absorbs certain amount of carbon dioxide. CO2 removal begins at temperatures above 250° C and continues until 800° C. Carbon dioxide binding involved both the outer and the inner surface of Zr-PILC, occurring in different locations, with different intensities. Zr-PILC dried at 200° C for 4 hours binds CO2 more strongly than the not dried Zr-PILC.. Przeprowadzono modyfikację montmorillonitu sodowego polikationami cyrkonowymi. W efekcie otrzymano mikroporowatą strukturę, stabilną termicznie oraz niepęczniejącą. Taki materiał może znaleźć zastosowanie w ochronie środowiska jako nośnik katalizatora w usuwaniu toksycznych lotnych chloropochodnych organicznych. Zbadano również możliwość wykorzystania Zr-PILC jako swoistego magazynu dla dwutlenku węgla. Analiza termiczna z analizą produktów gazowych wykazała, iż materiał ten zasorbował część dwutlenku węgla. Usuwanie CO2 rozpoczyna się w temperaturze powyżej 250°C i trwa do temperatury około 800°C. Dwutlenek węgla związał się zarówno z powierzchnią zewnętrzną, jak i wewnętrzną Zr-PILC w różnych miejscach, z różną siłą. Zr- PILC wysuszony w 200°C przez okres 4 godzin silniej wiąże CO2 w stosunku do Zr-PILC niesuszonego