Haloizyt podpierany polikationami metalo-hydroksylowymi - próba syntezy i właściwości

Abstract

Pillared clays have been an important factor in the technological study of matter for almost 35 years. Their sorption – catalysis and high temperature resistance properties are particularly valued. Although current studies have many positions on pillared montmorrilonites and kaolinites, little is known about pillared halloysite. This paper presents attempts of halloysite modification to obtain pillared material. Structural analysis was based on X-ray diffractometry (XRD) and IR spectrometry (FTIR). It was established that in the applied experimental conditions the intercalation of polycations into the halloysite interlayer space was not possible. In this thesis the analysis, studies and results are described and presented. Od blisko 35 lat podpierane minerały ilaste są ważnym elementem w różnych dziedzinach technologicznych. Cenione są przede wsystkim za ich szczególne właściwości sorpcyjo – katalityczne oraz wysoką odporność termiczną. O ile zakres literatury dotyczący podpieranych montmorrilonitów i kaolinitów jest obszerny, o tyle prace dotyczące podpierania haloizytu są nieliczne. W niniejszej pracy dyplomowej została opisana próba modyfikacji haloizytu w celu uzyskania materiału podpieranego. Analizę strukturalną przeprowadzono przy użyciu dyfraktometrii rentgenowskiej (XRD) oraz spektroskopii w podczerwieni (FTIR). Ustalono, iż w zastosowanych warunkach eksperymentalnych nie było możliwe wprowadzenie polikationów do przestrzeni międzypakietowej haloizytu. W pracy magisterskiej przedstawiono schemat oraz wyniki przeprowadzonych badań.