Microstructure and texture welds of 15-7Mo steel after heat treatment

Abstract

This paper presents the results of determining the effect of heat treatment after welding X8CrNiMoAl15-7-2 steel (commercial name: PH 15-7Mo steel) on the microstructure and texture of the welds. XRD studies showed the presence of the two phases in the welds of 15-7Mo steel, i.e., δ ferrite and austenite. Annealing at a temperature of 400°C/1 h and 550°C/1 h results in changes of the intensities for individual peaks derived from austenite and ferrite. Microstructure investigations carried out by LM and TEM indicated that the austenite and δ ferrite coexist in the microstructure of 15-7Mo steel in as-welded condition. Annealing at a temperature range of be- tween 400–620°C after welding causes small changes in the microstructure. The hardness of the welds after annealing in that temperature range increases.

W artykule zostały zaprezentowane wyniki badań wpływu obróbki cieplnej po spawaniu stali X8CrNiMoAl15-7-2 (nazwa handlowa: PH 15-7Mo) na mikrostrukturę i teksturę spoin. Badania XRD wykazały obecność dwóch faz w spoinach stali 15-7Mo, tj. ferrytu δ i austenitu. Wyżarzanie w temperaturach 400°C przez 1 h i 550°C przez 1 h powoduje zmiany intensywności poszczególnych pików pochodzących od austenitu i ferrytu. Badania mikrostrukturalne (mikroskopia świetlna i transmisyjna mikroskopia elektronowa) potwierdziły obecność ferrytu δ i austenitu w stali 15-7Mo w stanie po spawaniu. Wyżarzanie po spawaniu w temperaturach pomiędzy 400°C a 620°C powoduje małe zmiany w mikrostrukturze. Twardość spoin po wyżarzaniu w zakresie tych temperatur wzrasta.