New BOF slags containing sodium and manganese

Abstract

The nature and properties of slag and dust generated during the manufacture of pig iron indicate the two possibilities of their utilization: sintering or cold agglomerating with Portland cement. Both sinter and pellets can be recycled in the LD converter. It was introduced the concept of 'preformed synthetic slag' to use the recycling of waste. If the material contains components forming the eutectic properties similar to sinter or pellet (obtained outside the converter) it stimulates the creation of slag in the LD converter.The aim of this research is to address the best way to deal with manganese before the molten metal reaches the final stage of temperature and composition for casting. Ideally, the composition of the slag and dust produced by the BOF-LD can be adjusted so that the molten metal that reaches the secondary metallurgy contains over 1.0% manganese.

Charakter i możliwosci żużla i płynów powstających podczas wytwarzania surówki wskazują na dwie możliwości ich utylizacji: spiekanie lub aglomeracja z cementem portlandzkim. Zarówno spiek, jak i brykiety mogą być poddawane recyklingowi w konwertorze LD. Wprowadzono koncepcję 'preformed synthetic slag' do zastosowania recyklingu odpadów. Jeśli ten materiał zawiera składniki tworzące eutektykę z własnościami podobnymi do spieku lub pelet (uzyskanych poza konwertorem), to aktywizuje proces tworzenia żużla w konwertorze LD. Celem niniejszych badań jest znalezienie najlepszego sposobu radzenia sobie z manganem, zanim ciekły metal osiągnie końcowe parametry temperatury i składu do odlewania. Najlepiej gdy skład żużla i wytwarzanego przez konwertor pyłu mogą być dostosowane tak, aby ciekły metal, który trafia do obróbki pozapiecowej, zawierał ponad 1,0% manganu.