Comparative assessment of Al-Si alloy gassing degree with the application of the 'first bubble' and 'solidification under decreased pressure' methods

Abstract

All aluminum alloys in a liquid state are characterised by easy oxidation and absorption of hydrogen from the surroundings (which are the main reasons for casting defects). The amount of hydrogen adsorbed by a liquid alloy depends mainly on temperature and melting time. The performed investigations were aimed at comparing two known methods of measuring a metal gassing degree, the first bubble method and sample solidification under decreased pressure. Liquid metal melting and holding processes were performed under different conditions that caused variability of its gassing degree, resulting in a variability of purity and quality of the liquid metal. The investigations were carried out with using the hypoeutectic aluminum-silica AK7 alloy.

Wszystkie stopy aluminiowe w stanie ciekłym charakteryzują się łatwym utlenianiem i pochłanianiem wodoru z otaczającej atmosfery, co jest główną przyczyną wad odlewniczych. Ilość wodoru zaabsorbowanego przez ciekły stop zależy głównie od temperatury i czasu topienia. Przeprowadzone badania miały na celu porównanie dwóch znanych metod pomiaru stopnia zagazowania metalu, metodę pierwszego pęcherzyka oraz metodę krzepnięcia próbki pod obniżonym ciśnieniem. Proces topienia i przetrzymywania ciekłego metalu odbywał się w różnych warunkach, co powodowało zmienność stopnia zagazowania, a tym samym czystości i jakości ciekłego metalu. Wykonane badania zostały przeprowadzone z wykorzystaniem podeutektycznego stopu aluminium-krzem AK7.