Inoculation-induced change in carbides content in the columnar and equiaxed structure of centrifugally cast tubes from 32Ni-25Cr-Nb steel

Abstract

The properties of alloys used for centrifugally cast catalytic tubes depend on the stability of carbides hardening the alloy at an operating temperature. Tubes cast in centrifugal process are characterised by structure changing on the cross-section: the outer layer is composed of columnar crystals, while inner layer has the structure of equiaxed crystals. The properties of these two zones differ and have a major influence on the casting behaviour during operation. The aim of this study was to determine the volume fraction of Cr and Nb carbides in the zone of columnar and equiaxed crystals under different inoculation regimes. It was found that the type of the used microadditives changes the amount of carbides in the investigated zones of castings.

Własności stopów, stosowanych do odlewania odśrodkowego rur katalitycznych, wynikają z wysokiej stabilności węglików umacniających stop w temperaturze pracy. Rury wykonywane metodą odlewania odśrodkowego posiadają zmieniającą się na przekroju strukturę: warstwa zewnętrzna - strukturę kolumnową, a warstwa wewnętrzna - strukturę równoosiową. Własności obu tych stref są różne i mają istotne znaczenie dla zachowania się odlewów w temperaturze pracy. W pracy określono udział objętościowy węglików Cr i Nb w strefie kryształów kolumnowych i równoosiowych dla poszczególnych rodzajów modyfikacji. Stwierdzono, że rodzaj zastosowanych mikrododatków wpływa na zmiany ilości węglików w badanych strefach odlewów.