Strain in the upsetting process

Abstract

In the paper strain distribution in materials commonly referred to as soft materials (electrolytic copper 99,9 % Cu, annealed) and hard ones (steel 20, containing 0,2 % C) produced during hot upsetting process. Numerical calculations were performed with a use of commercial software QForm2D/3D. Significance of the influence of friction forces in the head surface on the free surface profile and distor-tion of rectangular coordination grid of deformations, as well as, effective strain distribution, in various stages of the process was investigated. The results indicate changes in nonuniformity of strain in obtained forgings.

W pracy analizowano rozkład odkształceń w materiałach potocznie zwanych miękkimi (miedź elektrolityczna Cu99,9E, zawierająca 99,90% Cu, stan miękki) lub twardymi (stal 20, zawierająca 0,2% C), powstającymi przy ich spęczaniu swobodnym na gorąco. Obliczenia numeryczne wykonano programem QFORM2D/3D. Wykazano istotny wpływ sił tarcia powierzchniowego na zmiany kształtu po-bocznicy i zniekształcenie linii siatki koordynacyjnej oraz rozkład intensywności odkształcenia na przekroju poprzecznym odkuwek, zachodzący w różnych fazach realizacji procesu spęczania. Wyniki te świadczą o przebiegu nierównomierności odkształcenia w spęczanych odkuwkach.