Analiza wpływu geometrii próbki na charakterystykę ściskania oraz charakter umocnienia stali kwasoodpornej X6CrNiTi18-10
(Data obrony: 2020-10-29) Kwaśniewska, Sara
Wydział Inżynierii Metali i Informatyki Przemysłowej
Access status: Open Access ,
Mechanical properties and corrosion resistance of cast NiAl alloys with the addition of Ti
(2015) Hyjek, Paweł; Sulima, Iwona; Malczewski, Piotr
Results of compression- and corrosion-resistance tests of NiAl alloys with 1.0 and 2.0 wt.% of titanium are described. The compression tests conducted at a wide range of temperatures, and the strain rate showed that an increase in titanium content causes increased brittleness at room temperature, while at higher temperatures, an increase of hardness and strength is observed. The analysis of electrochemical corrosion resistance showed that alloys containing Ti are characterized by considerable resistance to sulfuric acid VI, because the emerging titanium oxide prevents the active solubilization of the alloy. Besides, microstructure observations performed at various levels of deformation, which allowed us to identify the mechanisms responsible for fracture of the studied alloys.
Access status: Metadata only ,
Podstawy wytrzymałości materiałów – laboratorium
(2023) Jakóbczyk, Joanna
Wydział Inżynierii Lądowej i Gospodarki Zasobami; Centrum e-Learningu i Innowacyjnej Dydaktyki
Kurs został przygotowany z myślą o przyszłych inżynieriach, dla których znajomość parametrów wytrzymałościowych materiałów oraz sposobu ich wyznaczania jest fundamentalna. Kurs przeprowadzi Państwa przez pięć modułów, z których każdy poświęcony jest jednej z pięciu podstawowych statycznych prób wytrzymałościowych: <ol><li>Statycznej próbie rozciągania,</li><li>Statycznej próbie ściskania,</li><li> Statycznej próbie skręcania,</li><li>Statycznej próbie ścinania,</li><li>Statycznej próbie zginania.</ol>Kluczowym elementem jest dziewięć tutoriali nagranych w laboratorium badań wytrzymałościowych, prezentujące krok po kroku jak przygotować się do badania oraz jak je poprawnie przeprowadzić. Na kursie sprawdzicie Państwo swoją wiedzę w quizach z zakresu obsługi maszyn, etapów przeprowadzenia każdej z prób oraz zakresu teoretycznego. Kurs powstał także z myślą o nauczycielach, aby służyć jako wsparcie procesu dydaktycznego. Znajdziecie na nim Państwo zestawy z danymi do samodzielnego opracowania przez Studentów oraz protokoły do wypełnienia na zajęciach.
Access status: Open Access ,
The influence of SiC particle size on mechanical properties of aluminium matrix composites
(2017) Wąsik, Anna; Leszczyńska-Madej, Beata Katarzyna; Madej, Marcin
The main aim of this study was to determine the influence of SiC particle size on the mechanical properties of aluminum matrix composites. The reinforcing phase was introduced into the aluminum matrix in two different particle sizes: a coarse fraction with particle size ranging from 40 to 60 µm, and a fine fraction with particle size of less than 2 µm. The SiC particles were added in various quantities equal to 2.5, 5, 7.5, and 10 wt% in order to determine the influence of different contents of the reinforcing phase on the density, hardness, and compressive strength of the obtained composite materials. By using scanning electron microscopy (SEM), the microstructure observations were performed and allowed for defining the influence of matrix/reinforcement particle size ratio (PSR) on the distribution of reinforcement particles in the matrix. The Al-SiC composites were prepared through the conventional powder metallurgy technique, including compaction under a pressure of 300 MPa and a sintering process in a nitrogen atmosphere at 600°C. Applying the reinforcing phase with the particle size (40–60 µm) similar to matrix (<63 µm) allowed us to obtain a more-uniform distribution of SiC particles in the matrix than after introducing the fine fraction of reinforcement (2 µm). The mechanical properties of the Al-SiC composites increased with increases in the weight fraction of the reinforcing phase, wherein this effect is more visible for composites reinforced with SiC particles of finer gradation.
Access status: Open Access ,
The tensile strength properties of lithological variety of Polish copper ores
(2012) Nad, Alona; Brożek, Marian; Naziemiec, Zdzisław
Artykuł przedstawia wyniki badań rozdrabniania pojedynczych ziaren przez ściskanie. Badania przeprowadzono na przykładzie trzech litologicznych odmian rud miedzi z kopalń Legnicko-Głogowskiego Okręgu Miedziowego: dolomit, łupek i piaskowiec. Wytrzymałość ziaren na rozciąganie była określana za pomocą jednoosiowego ściskania. Wytrzymałość na rozciąganie mineralnych ziaren charakteryzuje się dużym rozrzutem wyników. Rozrzut ten jest spowodowany wpływem losowych czynników takich jak warunki obciążenia, ułożenie ziarna, kształt ziarna oraz wewnętrzna struktura ziarna. W związku z tym wytrzymałość zbioru ziaren mineralnych charakteryzuje się pewnym rozkładem. Dystrybuanta rozkładu wytrzymałości jest wyrażona przez rozkład Weibulla, w którym parametry rozkładu są niezależne od wielkości ziaren. W artykule również zaprezentowane zależności średniej wytrzymałości dolomitu, łupku i piaskowca od rozmiaru ziaren.
Access status: Restricted ,
Właściwości mechaniczne materiałów termoelektrycznych
(Data obrony: 2020-01-22) Kwaśniewska, Dominika
Wydział Inżynierii Materiałowej i Ceramiki