Mechanical properties and corrosion resistance of cast NiAl alloys with the addition of Ti

Abstract

Results of compression- and corrosion-resistance tests of NiAl alloys with 1.0 and 2.0 wt.% of titanium are described. The compression tests conducted at a wide range of temperatures, and the strain rate showed that an increase in titanium content causes increased brittleness at room temperature, while at higher temperatures, an increase of hardness and strength is observed. The analysis of electrochemical corrosion resistance showed that alloys containing Ti are characterized by considerable resistance to sulfuric acid VI, because the emerging titanium oxide prevents the active solubilization of the alloy. Besides, microstructure observations performed at various levels of deformation, which allowed us to identify the mechanisms responsible for fracture of the studied alloys. W artykule zamieszczono wyniki badań wytrzymałości i odporności na korozję stopów na osnowie fazy NiAl z dodatkiem 1.0 i 2.0% wag. tytanu. Prowadzone w szerokim zakresie temperatur i prędkości odkształcania próby ściskania wykazały, że wzrost zawartości tytanu wpływa na zwiększenie kruchości stopu w temperaturze pokojowej, podczas gdy w podwyższonych temperaturach obserwuje się zwiększenie twardości i wytrzymałości. Analiza odporności na korozję elektrochemiczną ujawniła, że stopy zawierające tytan charakteryzują się znaczą odpornością na działanie kwasu siarkowego VI, bowiem powstający tlenek tytanu utrudnia aktywne roztwarzanie stopu. Wykonano także obserwacje mikrostrukturalne na różnych poziomach odkształcenia, które pozwoliły na identyfikację mechanizmów odpowiedzialnych za zniszczenie (pękanie) stopów.