Badania korozyjności cieczy nadpakerowych na bazie chlorku sodu w warunkach dopływu siarkowodoru

Abstract

The authors present the results of experiments oriented to determining the corrosiveness of over-packer $Na-Cl$-based fluids, saturated with hydrogen sulfide, in the area of the BMB field, as well as the selection of the most efficient corrosion inhibitor. The experiments concentrated on the measurement of $H_{2}S$, pH and corrosiveness of over-packer fluids saturated with hydrogen sulfide at temperature 60 and 80 Celsius degrees. The experiments were conducted for two types of solutions: $NaCl$ and $NaCl+CMC LV$, with the initial pH mpos 10 and 12. Analogous experiments were performed for the above fluids after adding three corrosion inhibitors. The analysis of the results showed that the lowest corrosiveness in the hydrogen sulfide conditions at a temperature of 80 Celsius degrees was obtained for the $NaCl$-based fluid with CMC LV and admixture of the corrosion inhibitor ANTYKOR PP with the initial pH = 12. W niniejszym artykule przedstawiono wyniki badań, których celem było doświadczalne określenie korozyjności płynów nadpakerowych na bazie $NaCl$ stosowanych w odwiertach w rejonie złoża BMB po ich nasyceniu $H_{2}S$, a także dobór najskuteczniejszego inhibitora korozji. Przeprowadzone badania obejmowały pomiary absorpcji $H_{2}S$, zmian pH oraz korozyjności cieczy nadpakerowych nasyconych siarkowodorem w temperaturze 60 stopni i 80 stopni Celsjusza. Badania przeprowadzono dla dwóch typów cieczy: roztwór $NaCl$ oraz $NaCl+CMC LV$, o początkowym pH mpos 10 i 12. Przeprowadzono również badania ww. cieczy z dodatkiem trzech inhibitorów korozji. Na podstawie badań stwierdzono, że najniższą korozyjnością w warunkach dopływu siarkowodoru w temp. 80 stopni Celsjusza charakteryzuje się ciecz nadpakerowa na bazie $NaCl$ z dodatkiem CMC LV oraz inhibitora korozji ANTYKOR PP o początkowym pH = 12.