Characterization of microstructure and mechanical properties of laser-welded stainless steels
Date
Presentation Date
Editor
Other contributors
Other title
Charakterystyka struktury i właściwości mechanicznych złączy spawanych wiązką laserową stali nierdzewnych
Resource type
Version
Pagination/Pages:
Research Project
Description
Abstract
This work presents the laser welding of dissimilar X12CrCoWVNbN12-2-2 and X10CrNi18-10 steels. This system is of interest, as laser welding offers new flexibility in the joining of metals and laser welds (LWs) and are usually of high quality, they are obtained only after the optimization of process parameters. The aim of the work was to investigate the microstructure, chemical composition, and hardness changes of laser-welded steels. After laser welding, two zones were generated in the processed materials: a fusion zone and a heat-affected zone. Due to solidification, a refinement of the microstructure occurred in the fusion zone. Examinations of the chemical composition of particular melted areas showed the occurrence of Nb-rich precipitations. The laser welding of steels led to increased hardness in the fusion zone (about 240–530 HV0.3).
W pracy przedstawiono wyniki badań różnorodnych złączy spawanych wiązką laserową stali X12CrCoWVNbN12-2-2 i X10CrNi18-10. Zastosowanie wiązki laserowej jest wysoce użyteczne ze względu na nowe możliwości procesu wytwarzania i zwykle wysoką jakość złączy po optymalizacji procesu. Celem pracy była ocena mikrostruktury, składu chemicznego i zmian twardości w złączach spawanych wiązką lasera. Po procesie spawania zaobserwowano dwa główne obszary, tj. linię wtopienia i strefę wpływu ciepła. Podczas krystalizacji w obszarze przy linii wtopienia zaobserwowano rozdrobnienie struktury. Szczegółowa analiza składu chemicznego ujawniła występowania wydzieleń bogatych w Nb w obszarze metalu stopionego. Zaobserwowano, że spawanie laserowe prowadzi do wzrostu twardości w obszarze przy linii wtopienia.