The influence of strain rate on microstructure and mechanical behavior of P/M feal

Abstract

As part of a broader study of the thermomechanical processing of P/M FeAl alloys, this research is focused on the influence of processing strain rate on the microstructural evolution and mechanical behavior of the processed materials. For the purposes of this study, water atomized FeAl powder was consolidated by hot pressing resulting in fully dense products. The consolidated P/M samples were thermomechanically processed in compression at 800 and 900oC at strain rates of 0.1 s-1 and 10 s-1, to a true strain of 1. The influence of thermomechanical processing parameters on the material flow and microstructural development of investigated alloy was analyzed. Considerable strain rate sensitivity of investigated alloy was observed, specially with reference to microstructural development. W niniejszej pracy przedstawiono wybrane wyniki badań wpływu prędkości odkształcenia na rozwój mikrostruktury oraz charakter odkształcenia plastycznego stopu z grupy FeAl. W badaniach zastosowano rozpylany wodą proszek stopu. W pełni zagęszczone poprzez prasowanie na gorąco próbki z proszków poddano próbie ściskania w temperaturach 800°C oraz 900°C przy prędkościach odkształcenia równych 0.1 s(-1) oraz 10 s(-1), do wartości odkształcenia rzeczywistego równej 1. W materiałach odkształconych w temperaturze 800°C rozdrobnienie mikrostruktury nastąpiło tylko przy większej prędkości odkształcenia (10 s(-1) ), natomiast w temperaturze 900°C materiał uległ rekrystalizacji niezależnie od prędkości odkształcenia. Badania wykazały stosunkowo dużą czułość stopu na prędkość odkształcenia, szczególnie w odniesieniu do zmian strukturalnych związanych z procesami rekrystalizacji.