The high-temperature tribology of iron matrix hypoeutectic alloy after under-annealing normalizing

Abstract

This work includes the results of high-temperature tribology test of cast alloy with iron matrix. The paper presents the discussion on the results of the studies of wear mechanisms and friction factor of G200CrNiMo4-3-3 adamite cast steel after three variants of under - annealing normalization. During the heat treatment of cast steel four annealing temperatures were applied: 850, 900, 950 and 1050°C. Annealing was conducted for 10 h, and then the samples were cooled at a rate of 48°C/h to room temperature. Four different annealing temperatures resulted in adequate differences in microstructure of test cast steel what determinated tribological properties of the material. Results obtained allow for determination of optimal, from wear resistance point of view, microstructure of test cast steel used for mill rolls. Niniejsza praca zawiera wyniki wysokotemperaturowego testu tribologicznego stopu odlewanego na osnowie żelaza. W pracy tej przedstawiono dyskusję wyników badań mechanizmów zużycia oraz współczynnika tarcia staliwa adamitowego G20CrNiMo4-3-3 po trzech wariantach normalizowania niezupełnego. Podczas obróbki cieplnej staliwa zastosowano cztery temperatury wyżarzania: 850, 900, 950 i 1050°C. Wyżarzanie prowadzono przez 10 h, później próbki chłodzono z szybkością 48°C/h do temperatury pokojowej. Cztery różne temperatury wyżarzania spowodowały odpowiednie różnice w mikrostrukturze badanego staliwa, co z kolei zdeterminowało własności tribologiczne materiału. Uzyskane wyniki badań pozwalają na określenie optymalnej, z punktu widzenia odporności na zużycie, mikrostruktury badanego staliwa, stosowanego na walce hutnicze.